- 密度 [g/cm3]: 1.05
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.130
- 热变形温度 [℃]: 42.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 28 | 28 | ASTM D785 | ||
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ISO 527 | ||
| Flexural Modulus | 0.130 GPa | 18.9 ksi | ASTM D790 | ||
| Izod Impact, Notched | NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ASTM D256 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D256 | |||
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D256 | |||
| Charpy Impact Unnotched | >= 30.0 J/cm² @Temperature -20.0 °C | >= 143 ft-lb/in² @Temperature -4.00 °F | DIN 53453 | ||
| >= 30.0 J/cm² @Temperature -40.0 °C | >= 143 ft-lb/in² @Temperature -40.0 °F | DIN 53453 | |||
| >= 30.0 J/cm² @Temperature 23.0 °C | >= 143 ft-lb/in² @Temperature 73.4 °F | DIN 53453 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 1000 ohm | 1000 ohm | IEC 93 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 34.0 °C | 93.2 °F | ASTM D648 | ||
| Vicat Softening Point | 49.0 °C | 120 °F | 50°C/h 50N; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Temperature can be reduced when using vacuum ovens. | ||
| Dry Time | >= 3 hour | >= 3 hour | Drying time can be reduced when using vacuum ovens. | ||
| Descriptive Properties | |||||
| Injection Speed | medium | ||||