- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.157
- 拉伸强度 [MPa]: 71.7
- 断裂伸长率 [%]: 68.9
- 弯曲强度 [MPa]: 44.1
- 弯曲模量 [MPa]: 1.79
- 热变形温度 [℃]: 94.4
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.19 g/cc | 0.0415 - 0.0430 lb/in³ | Average value: 1.18 g/cc Grade Count:17 |
| Water Absorption | 0.300 - 2.00 % | 0.300 - 2.00 % | Average value: 0.490 % Grade Count:10 |
| Water Absorption at Saturation | 0.300 % | 0.300 % | Average value: 0.300 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00200 - 0.00700 cm/cm | 0.00200 - 0.00700 in/in | Average value: 0.00423 cm/cm Grade Count:15 |
| Melt Flow | 0.900 - 19.0 g/10 min | 0.900 - 19.0 g/10 min | Average value: 3.78 g/10 min Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 44.0 - 105 | 44.0 - 105 | Average value: 85.7 Grade Count:14 |
| Tensile Strength, Ultimate | 44.1 - 80.0 MPa | 6400 - 11600 psi | Average value: 67.0 MPa Grade Count:14 |
| Tensile Strength, Yield | 71.7 - 76.0 MPa | 10400 - 11000 psi | Average value: 74.4 MPa Grade Count:3 |
| Elongation at Break | 3.00 - 30.0 % | 3.00 - 30.0 % | Average value: 13.3 % Grade Count:11 |
| Elongation at Yield | 4.00 - 13.0 % | 4.00 - 13.0 % | Average value: 6.14 % Grade Count:7 |
| Modulus of Elasticity | 1.72 - 3.60 GPa | 250 - 522 ksi | Average value: 2.86 GPa Grade Count:14 |
| Flexural Yield Strength | 68.9 - 133 MPa | 10000 - 19300 psi | Average value: 103 MPa Grade Count:15 |
| Flexural Modulus | 1.79 - 3.43 GPa | 260 - 498 ksi | Average value: 2.87 GPa Grade Count:14 |
| Izod Impact, Notched | 0.157 - 0.534 J/cm | 0.294 - 1.00 ft-lb/in | Average value: 0.280 J/cm Grade Count:13 |
| 0.240255 - 0.32034 J/cm @Temperature 0.000 - 0.000 °C | 0.450096 - 0.60013 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.274 J/cm Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 18.7 - 20.0 kV/mm | 475 - 508 kV/in | Average value: 19.6 kV/mm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 59.9 - 75.0 µm/m-°C | 33.3 - 41.7 µin/in-°F | Average value: 65.0 µm/m-°C Grade Count:3 |
| 72.0 - 90.0 µm/m-°C @Temperature 0.000 - 156 °C | 40.0 - 50.0 µin/in-°F @Temperature 32.0 - 312 °F | Average value: 76.5 µm/m-°C Grade Count:4 | |
| Thermal Conductivity | 0.187 - 0.210 W/m-K | 1.30 - 1.46 BTU-in/hr-ft²-°F | Average value: 0.194 W/m-K Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.4 - 113 °C | 202 - 235 °F | Average value: 102 °C Grade Count:8 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 - 108 °C | 185 - 226 °F | Average value: 97.4 °C Grade Count:14 |
| Vicat Softening Point | 95.0 - 119 °C | 203 - 246 °F | Average value: 107 °C Grade Count:16 |
| Flammability, UL94 | HB | HB | Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 - 1.51 | 1.49 - 1.51 | Average value: 1.49 Grade Count:12 |
| Haze | 0.300 - 96.0 % | 0.300 - 96.0 % | Average value: 9.32 % Grade Count:12 |
| Yellow Index | 0.300 - 5.50 % | 0.300 - 5.50 % | Average value: 1.60 % Grade Count:4 |
| Transmission, Visible | 80.0 - 93.0 % | 80.0 - 93.0 % | Average value: 90.9 % Grade Count:17 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | Average value: 240 °C Grade Count:5 |
| Mold Temperature | 43.3 - 90.0 °C | 110 - 194 °F | Average value: 65.2 °C Grade Count:5 |
| Drying Temperature | 82.2 - 109 °C | 180 - 228 °F | Average value: 87.6 °C Grade Count:5 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.50 hour Grade Count:5 |