- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 39.3
- 断裂伸长率 [%]: 44.0
- 弯曲强度 [MPa]: 33.0
- 弯曲模量 [MPa]: 2.21
- 硬度: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 - 1.49 g/cc | 0.0452 - 0.0538 lb/in³ | Average value: 1.36 g/cc Grade Count:34 |
| Water Absorption | 0.0600 - 0.0700 % | 0.0600 - 0.0700 % | Average value: 0.0633 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00468 cm/cm Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 82.0 - 110 | 82.0 - 110 | Average value: 97.8 Grade Count:27 |
| Tensile Strength, Ultimate | 33.0 - 53.0 MPa | 4790 - 7690 psi | Average value: 43.6 MPa Grade Count:28 |
| Tensile Strength, Yield | 39.3 - 40.7 MPa | 5700 - 5900 psi | Average value: 40.1 MPa Grade Count:7 |
| Elongation at Break | 55.0 - 195 % | 55.0 - 195 % | Average value: 128 % Grade Count:19 |
| Modulus of Elasticity | 1.87 - 2.90 GPa | 271 - 420 ksi | Average value: 2.36 GPa Grade Count:21 |
| Flexural Yield Strength | 44.0 - 76.0 MPa | 6380 - 11000 psi | Average value: 66.1 MPa Grade Count:34 |
| Flexural Modulus | 2.21 - 3.10 GPa | 320 - 449 ksi | Average value: 2.47 GPa Grade Count:15 |
| Izod Impact, Notched | 0.320 - 9.60 J/cm | 0.599 - 18.0 ft-lb/in | Average value: 5.49 J/cm Grade Count:33 |
| 0.500 - 1.0678 J/cm @Temperature -29.0 - 0.000 °C | 0.937 - 2.0004 ft-lb/in @Temperature -20.2 - 32.0 °F | Average value: 0.784 J/cm Grade Count:2 | |
| Taber Abrasion, mg/1000 Cycles | 0.0380 | 0.0380 | Average value: 0.0380 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 38.3 - 101 µm/m-°C | 21.3 - 56.0 µin/in-°F | Average value: 79.9 µm/m-°C Grade Count:8 |
| 75.6 - 75.6 µm/m-°C @Temperature 16.0 - 16.0 °C | 42.0 - 42.0 µin/in-°F @Temperature 60.8 - 60.8 °F | Average value: 75.6 µm/m-°C Grade Count:1 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 - 82.0 °C | 150 - 180 °F | Average value: 74.8 °C Grade Count:34 |
| UL RTI, Electrical | 50.0 °C | 122 °F | Average value: 50.0 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | Average value: 50.0 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | Average value: 50.0 °C Grade Count:4 |
| Flammability, UL94 | V-0 - 5VA | V-0 - 5VA | Grade Count:20 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 200 °C | 320 - 392 °F | Average value: 179 °C Grade Count:19 |
| Adapter Temperature | 171 - 177 °C | 340 - 350 °F | Average value: 174 °C Grade Count:4 |
| Die Temperature | 171 - 177 °C | 340 - 350 °F | Average value: 174 °C Grade Count:4 |
| Melt Temperature | 157 - 207 °C | 315 - 405 °F | Average value: 182 °C Grade Count:6 |
| Dry Time | 0.000 - 4.00 hour | 0.000 - 4.00 hour | Average value: 1.33 hour Grade Count:6 |