- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 60.0
- 断裂伸长率 [%]: 48.3
- 弯曲强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 91.0
- 透光率 [%]: 84.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.19 g/cc | 0.0401 - 0.0430 lb/in³ | Average value: 1.18 g/cc Grade Count:132 |
| Water Absorption | 0.300 % | 0.300 % | Average value: 0.300 % Grade Count:23 |
| Water Absorption at Saturation | 0.300 - 2.00 % | 0.300 - 2.00 % | Average value: 0.867 % Grade Count:3 |
| Particle Size | 230 - 600 µm | 230 - 600 µm | Average value: 538 µm Grade Count:6 |
| Viscosity | 2.00e+6 - 2.00e+6 cP @Temperature 240 - 240 °C | 2.00e+6 - 2.00e+6 cP @Temperature 464 - 464 °F | Average value: 2.00e+6 cP Grade Count:1 |
| 2.00e+6 - 2.00e+6 cP @Shear Rate 100 - 100 1/s | 2.00e+6 - 2.00e+6 cP @Shear Rate 100 - 100 1/s | Average value: 2.00e+6 cP Grade Count:1 | |
| Linear Mold Shrinkage | 0.00200 - 0.00800 cm/cm | 0.00200 - 0.00800 in/in | Average value: 0.00420 cm/cm Grade Count:130 |
| Melt Flow | 0.700 - 40.0 g/10 min | 0.700 - 40.0 g/10 min | Average value: 10.7 g/10 min Grade Count:131 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 48.0 - 99.0 | 48.0 - 99.0 | Average value: 85.3 Grade Count:30 |
| Tensile Strength, Ultimate | 38.0 - 89.3 MPa | 5510 - 13000 psi | Average value: 59.5 MPa Grade Count:125 |
| Tensile Strength, Yield | 60.0 - 72.0 MPa | 8700 - 10400 psi | Average value: 69.4 MPa Grade Count:7 |
| Elongation at Break | 2.00 - 40.0 % | 2.00 - 40.0 % | Average value: 8.79 % Grade Count:125 |
| Elongation at Yield | 2.00 - 6.00 % | 2.00 - 6.00 % | Average value: 3.65 % Grade Count:10 |
| Modulus of Elasticity | 1.76 - 3.65 GPa | 255 - 530 ksi | Average value: 2.86 GPa Grade Count:124 |
| Flexural Yield Strength | 48.3 - 124 MPa | 7000 - 18000 psi | Average value: 94.3 MPa Grade Count:131 |
| Flexural Modulus | 2.00 - 3.45 GPa | 290 - 500 ksi | Average value: 2.96 GPa Grade Count:20 |
| Izod Impact, Notched | 0.160 - 1.30 J/cm | 0.300 - 2.44 ft-lb/in | Average value: 0.306 J/cm Grade Count:125 |
| 0.26695 - 0.800 J/cm @Temperature 0.000 - 0.000 °C | 0.50011 - 1.50 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.516 J/cm Grade Count:3 | |
| 0.26695 - 0.800 J/cm @Diameter 6.35 - 6.35 mm | 0.50011 - 1.50 ft-lb/in @Diameter 0.250 - 0.250 in | Average value: 0.516 J/cm Grade Count:3 | |
| Izod Impact, Notched (ISO) | 1.70 - 2.20 kJ/m² | 0.809 - 1.05 ft-lb/in² | Average value: 1.85 kJ/m² Grade Count:6 |
| Charpy Impact Unnotched | 1.80 - 2.60 J/cm² | 8.57 - 12.4 ft-lb/in² | Average value: 2.00 J/cm² Grade Count:6 |
| Charpy Impact, Notched | 0.200 - 1.80 J/cm² | 0.952 - 8.57 ft-lb/in² | Average value: 0.592 J/cm² Grade Count:9 |
| Gardner Impact | 0.226 - 9.04 J | 0.167 - 6.67 ft-lb | Average value: 1.58 J Grade Count:106 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.40 - 3.80 | 3.40 - 3.80 | Average value: 3.67 Grade Count:8 |
| Dielectric Strength | 18.0 - 45.0 kV/mm | 457 - 1140 kV/in | Average value: 21.4 kV/mm Grade Count:8 |
| Dissipation Factor | 0.0400 - 0.0500 | 0.0400 - 0.0500 | Average value: 0.0471 Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 120 µm/m-°C | 16.7 - 66.7 µin/in-°F | Average value: 68.9 µm/m-°C Grade Count:127 |
| 72.0 - 72.0 µm/m-°C @Temperature 0.000 - 156 °C | 40.0 - 40.0 µin/in-°F @Temperature 32.0 - 312 °F | Average value: 72.0 µm/m-°C Grade Count:2 | |
| Specific Heat Capacity | 1.30 - 1.50 J/g-°C | 0.311 - 0.359 BTU/lb-°F | Average value: 1.44 J/g-°C Grade Count:11 |
| 1.90 - 2.30 J/g-°C @Temperature 100 - 175 °C | 0.454 - 0.550 BTU/lb-°F @Temperature 212 - 347 °F | Average value: 2.10 J/g-°C Grade Count:3 | |
| Thermal Conductivity | 0.190 - 0.220 W/m-K | 1.32 - 1.53 BTU-in/hr-ft²-°F | Average value: 0.205 W/m-K Grade Count:11 |
| Melting Point | 132 - 157 °C | 270 - 315 °F | Average value: 150 °C Grade Count:7 |
| Maximum Service Temperature, Air | 50.0 - 100 °C | 122 - 212 °F | Average value: 78.1 °C Grade Count:61 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 - 106 °C | 196 - 223 °F | Average value: 100 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 104 °C | 140 - 220 °F | Average value: 85.2 °C Grade Count:132 |
| Vicat Softening Point | 75.6 - 117 °C | 168 - 243 °F | Average value: 102 °C Grade Count:122 |
| Flammability, UL94 | HB | HB | Grade Count:79 |
| Glow Wire Test | 650 °C | 1200 °F | Average value: 650 °C Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 - 1.51 | 1.49 - 1.51 | Average value: 1.49 Grade Count:22 |
| Haze | 0.400 - 12.0 % | 0.400 - 12.0 % | Average value: 1.41 % Grade Count:122 |
| Yellow Index | -0.400 - 1.00 % | -0.400 - 1.00 % | Average value: 0.750 % Grade Count:8 |
| Transmission, Visible | 84.0 - 92.0 % | 84.0 - 92.0 % | Average value: 91.6 % Grade Count:132 |
| UV Transmittance | 49.5 - 88.5 % | 49.5 - 88.5 % | Average value: 75.2 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 193 - 260 °C | 380 - 500 °F | Average value: 233 °C Grade Count:8 |
| Mold Temperature | 26.7 - 79.4 °C | 80.0 - 175 °F | Average value: 55.0 °C Grade Count:7 |
| Drying Temperature | 71.1 - 79.4 °C | 160 - 175 °F | Average value: 77.5 °C Grade Count:7 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.50 hour Grade Count:7 |