- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 46.9
- 弯曲强度 [MPa]: 36.3
- 弯曲模量 [MPa]: 1.65
- 热变形温度 [℃]: 85.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 - 1.17 g/cc | 0.0390 - 0.0423 lb/in³ | Average value: 1.13 g/cc Grade Count:13 |
| Water Absorption | 0.300 - 2.00 % | 0.300 - 2.00 % | Average value: 0.709 % Grade Count:9 |
| Linear Mold Shrinkage | 0.00300 - 0.00800 cm/cm | 0.00300 - 0.00800 in/in | Average value: 0.00543 cm/cm Grade Count:7 |
| Melt Flow | 1.60 - 12.3 g/10 min | 1.60 - 12.3 g/10 min | Average value: 5.58 g/10 min Grade Count:13 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 27.0 - 60.0 | 27.0 - 60.0 | Average value: 37.8 Grade Count:6 |
| Tensile Strength, Ultimate | 36.3 - 50.3 MPa | 5270 - 7300 psi | Average value: 43.4 MPa Grade Count:11 |
| Elongation at Break | 5.00 - 40.0 % | 5.00 - 40.0 % | Average value: 20.6 % Grade Count:11 |
| Elongation at Yield | 3.60 - 4.50 % | 3.60 - 4.50 % | Average value: 3.99 % Grade Count:7 |
| Modulus of Elasticity | 1.38 - 2.96 GPa | 200 - 430 ksi | Average value: 2.06 GPa Grade Count:13 |
| Flexural Yield Strength | 46.9 - 99.3 MPa | 6800 - 14400 psi | Average value: 66.1 MPa Grade Count:11 |
| Flexural Modulus | 1.65 - 2.45 GPa | 240 - 355 ksi | Average value: 2.08 GPa Grade Count:7 |
| Izod Impact, Notched | 0.320 - 1.23 J/cm | 0.600 - 2.30 ft-lb/in | Average value: 0.776 J/cm Grade Count:11 |
| 0.42712 - 0.58729 J/cm @Temperature 0.000 - 0.000 °C | 0.80017 - 1.1002 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.534 J/cm Grade Count:3 | |
| 0.42712 - 0.58729 J/cm @Diameter 6.35 - 6.35 mm | 0.80017 - 1.1002 ft-lb/in @Diameter 0.250 - 0.250 in | Average value: 0.534 J/cm Grade Count:3 | |
| Gardner Impact | 3.05 - 7.34 J | 2.25 - 5.42 ft-lb | Average value: 5.20 J Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 - 100 µm/m-°C | 40.0 - 55.6 µin/in-°F | Average value: 88.4 µm/m-°C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 - 90.0 °C | 185 - 194 °F | Average value: 87.6 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 85.6 °C | 158 - 186 °F | Average value: 78.9 °C Grade Count:13 |
| Vicat Softening Point | 80.0 - 112 °C | 176 - 234 °F | Average value: 95.1 °C Grade Count:13 |
| Flammability, UL94 | HB | HB | Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 - 1.51 | 1.49 - 1.51 | Average value: 1.50 Grade Count:5 |
| Haze | 2.00 - 7.00 % | 2.00 - 7.00 % | Average value: 4.29 % Grade Count:7 |
| Yellow Index | -1.00 - -0.300 % | -1.00 - -0.300 % | Average value: -0.440 % Grade Count:5 |
| Transmission, Visible | 80.0 - 91.0 % | 80.0 - 91.0 % | Average value: 88.0 % Grade Count:13 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 249 °C | 360 - 480 °F | Average value: 223 °C Grade Count:5 |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | Average value: 65.6 °C Grade Count:5 |
| Drying Temperature | 71.1 - 79.4 °C | 160 - 175 °F | Average value: 74.4 °C Grade Count:5 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.50 hour Grade Count:5 |