- 熔体流动速率 [g/10min]: 1.8
- 缺口冲击强度: 1.23
- 弯曲模量 [MPa]: 1.86
- 透光率 [%]: 87.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.40 % | <= 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D951 |
| Melt Flow | 1.8 g/10 min @Load 5.00 kg, Temperature 230 °C | 1.8 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 47 | 47 | ASTM D785 |
| Tensile Strength at Break | 36.3 MPa | 5270 psi | ASTM D638 |
| Elongation at Break | 13.9 % | 13.9 % | ASTM D638 |
| Elongation at Yield | 3.8 % | 3.8 % | ASTM D638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM D638 |
| Flexural Strength | 67.6 MPa | 9800 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Diameter 6.35 mm | 2.30 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 95.4 µm/m-°C @Temperature 0.000 - 100 °C | 53.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 6.35 mm | 158 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Yellow Index | -0.300 % | -0.300 % | ASTM E313 |
| Transmission, Visible | 87 % | 87 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 210 - 249 °C | 410 - 480 °F | Cylinder Temp |
| Melt Temperature | 216 - 249 °C | 420 - 480 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |