- 熔体流动速率 [g/10min]: 1.9
- 缺口冲击强度: 13.9
- 弯曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.26 % | <= 0.26 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D951 |
| Melt Flow | 1.9 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.9 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 44 | 44 | ASTM D785 |
| Tensile Strength at Break | 54.2 MPa | 7860 psi | ASTM D638 |
| Elongation at Break | 88 % | 88 % | ASTM D638 |
| Elongation at Yield | 4.2 % | 4.2 % | ASTM D638 |
| Tensile Modulus | 2.07 GPa | 300 ksi | ASTM D638 |
| Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 13.9 J/cm @Diameter 3.17 mm | 26.1 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 |
| 9.13 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 17.1 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | BAR; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 93.6 µm/m-°C @Temperature 0.000 - 100 °C | 52.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C @Thickness 6.35 mm | 217 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 135 °C | 275 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 0.0 % | 0.0 % | Opaque; ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 199 - 266 °C | 390 - 510 °F | Cylinder Temp |
| Melt Temperature | 238 - 266 °C | 460 - 510 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |