- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 1.15
- 缺口冲击强度: 0.53
- 断裂伸长率 [%]: 69.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 1.90
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D551 |
| Melt Flow | 1.6 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.6 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45 | 45 | ASTM D785 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.90 GPa | 276 ksi | ASTM D638 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Diameter 6.35 mm | 0.993 ft-lb/in @Diameter 0.250 in | bar; ASTM D256 |
| 0.270 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 0.506 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 100 °C | 40.0 µin/in-°F @Temperature 32.0 - 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 - 248 °C | 450 - 478 °F | |