- 熔体流动速率 [g/10min]: 7.0
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.192
- 弯曲模量 [MPa]: 3.38
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ASTM D1895 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 7.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | ASTM D638 |
| Elongation at Yield | 4.0 - 6.0 % | 4.0 - 6.0 % | ASTM D638 |
| Tensile Modulus | 3.24 GPa | 470 ksi | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.38 GPa | 490 ksi | ASTM D790 |
| Izod Impact, Notched | 0.192 J/cm @Temperature 23.0 °C | 0.360 ft-lb/in @Temperature 73.4 °F | 1/4" bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 156 °C | 40.0 µin/in-°F @Temperature 32.0 - 312 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 6.35 mm | 201 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Yellow Index | <= 1.0 % | <= 1.0 % | ASTM D1925 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
| UV Transmittance | >= 87.7 % | >= 87.7 % | 340 nm |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | |
| Mold Temperature | 32.2 - 79.4 °C | 90.0 - 175 °F | |
| Drying Temperature | 76.7 °C | 170 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |