- 缺口冲击强度: 0.166
- 拉伸强度 [MPa]: 78.6
- 透光率 [%]: 93.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 94 | 94 | Control; ASTM D785 |
| 94 | 94 | Sterrad Processed; ASTM D785 | |
| Tensile Strength, Yield | 78.6 MPa | 11400 psi | Sterrad Processed; ASTM D638 |
| 80.25 MPa | 11640 psi | Control; ASTM D638 | |
| 71.64 MPa @Strain 1.20 % | 10390 psi @Strain 1.20 % | Control;Chemical Resistance to lipids, 24hrs, 30°C; ASTM D638 | |
| 77.84 MPa @Strain 1.20 % | 11290 psi @Strain 1.20 % | Control;Chemical Resistance to lipids, 24hrs, 30°C; ASTM D638 | |
| Elongation at Break | 5.5 % | 5.5 % | Sterrad Processed; ASTM D638 |
| 5.9 % | 5.9 % | Sterrad Processed; Chemical Resistance to lipids, 1.2% strain, 24hrs, 30°C+I9175; ASTM D638 | |
| 10.3 % | 10.3 % | Control; ASTM D638 | |
| 11.8 % | 11.8 % | Control;Chemical Resistance to lipids, 1.2% strain, 24hrs, 30°C; ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | Sterrad Processed; ASTM D638 |
| 5.7 % | 5.7 % | Control; ASTM D638 | |
| Tensile Modulus | 3.24 GPa | 470 ksi | Control; ASTM D638 |
| 3.26 GPa | 473 ksi | Sterrad Processed; ASTM D638 | |
| Izod Impact, Notched | 0.166 J/cm @Thickness 3.17 mm | 0.310 ft-lb/in @Thickness 0.125 in | Sterrad Processed; ASTM D256 |
| 0.192 J/cm @Thickness 3.17 mm | 0.360 ft-lb/in @Thickness 0.125 in | Control; ASTM D256 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | Control; ASTM D542 |
| 1.49 | 1.49 | Sterrad Processed; ASTM D542 | |
| Haze | 0.70 % | 0.70 % | Control; ASTM D1003 |
| 0.90 % | 0.90 % | Sterrad Processed; ASTM D1003 | |
| Gloss | 137 % | 137 % | 60°, Control; ASTM D523 |
| 138 % | 138 % | 60°, Sterrad Processed; ASTM D523 | |
| Yellow Index | 0.30 % | 0.30 % | Sterrad Processed; ASTM D1003 |
| 0.40 % | 0.40 % | Control; ASTM D1003 | |
| Transmission, Visible | 93 % | 93 % | Sterrad Processed; ASTM D1003 |
| 93 % | 93 % | Control; ASTM D1003 | |