- 熔体流动速率 [g/10min]: 16.0
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 46.1
- 弯曲模量 [MPa]: 2.10
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D551 |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 230 °C | 16 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 18 | 18 | ASTM D785 |
| Tensile Strength, Yield | 46.1 MPa | 6690 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ASTM D638 |
| Flexural Strength | 66.9 MPa | 9700 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm, Temperature 0.000 °C | 1.30 ft-lb/in @Thickness 0.250 in, Temperature 32.0 °F | ASTM D256 |
| 0.961 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature 0.000 - 100 °C | 50.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C | 178 °F | ASTM D648 |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.515 | 1.515 | ASTM D542 |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |