- 熔体流动速率 [g/10min]: 2.4
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.214
- 拉伸强度 [MPa]: 63.4
- 弯曲模量 [MPa]: 3.03
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.4 g/10 min @Load 5.00 kg, Temperature 200 °C | 2.4 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 76 - 80 | 76 - 80 | ASTM D785 |
| Tensile Strength, Yield | 63.4 MPa | 9200 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.03 GPa | 440 ksi | ASTM D638 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |