Evonik CYRO Acrylite® H10 Acrylic molding and extrusion compound

Evonik CYRO Acrylite® H10 Acrylic molding and extrusion compound 物性表: Evonik CYRO Acrylite® H10 Acrylic molding and extrusion compound物性表及特性介绍,Evonik CYRO Acrylite® H10 Acrylic molding and extrusion compound注塑参数详情,如需Evonik CYRO Acrylite® H10 Acrylic molding and extrusion compound下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 14.0
  • 缺口冲击强度: 0.133
  • 拉伸强度 [MPa]: 70.3
  • 弯曲模量 [MPa]: 3.40
  • 透光率 [%]: 92.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.19 g/cc1.19 g/ccASTM D792
Water Absorption <= 0.30 %<= 0.30 %ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm0.0030 - 0.0060 in/inASTM D551
Melt Flow 14 g/10 min
@Load 3.80 kg,
Temperature 230 °C
14 g/10 min
@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 9090ASTM D785
Tensile Strength, Yield 70.3 MPa10200 psiASTM D638
Elongation at Break 2.5 %2.5 %ASTM D638
Elongation at Yield 2.5 %2.5 %ASTM D638
Tensile Modulus 3.70 GPa537 ksiASTM D638
Flexural Strength 67.9 MPa9850 psiASTM D790
Flexural Modulus 3.40 GPa493 ksiASTM D790
Izod Impact, Notched 0.133 J/cm
@Temperature 23.0 °C
0.250 ft-lb/in
@Temperature 73.4 °F
ASTM D256
 
Thermal PropertiesMetricEnglishComments
CTE, linear 61.2 µm/m-°C
@Temperature -30.0 - 30.0 °C
34.0 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 91.1 °C196 °FASTM D648
Vicat Softening Point 104 °C219 °FASTM D1525
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.491.49ASTM D542
Haze <= 1.0 %<= 1.0 %ASTM D1003
Transmission, Visible 92 %92 %ASTM D1003

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-30087.html

免责声明: 本文 Evonik CYRO Acrylite® H10 Acrylic molding and extrusion compound 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4