- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.88
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 8.96
- 断裂伸长率 [%]: 17.0
- 弯曲强度 [MPa]: 10.3
- 弯曲模量 [MPa]: 0.172
- 硬度: 49.0
- 热变形温度 [℃]: 69.4
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.880 - 1.14 g/cc | 0.0318 - 0.0412 lb/in³ | Average value: 0.919 g/cc Grade Count:173 |
| Water Absorption | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0155 % Grade Count:20 |
| Thickness | 50.0 - 102 microns | 1.97 - 4.00 mil | Average value: 72.2 microns Grade Count:7 |
| Linear Mold Shrinkage | 0.00400 - 0.0252 cm/cm | 0.00400 - 0.0252 in/in | Average value: 0.0154 cm/cm Grade Count:49 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0170 - 0.0250 cm/cm | 0.0170 - 0.0250 in/in | Average value: 0.0223 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.00110 - 0.0263 cm/cm | 0.00110 - 0.0263 in/in | Average value: 0.0169 cm/cm Grade Count:11 |
| Melt Flow | 0.300 - 100 g/10 min | 0.300 - 100 g/10 min | Average value: 17.9 g/10 min Grade Count:212 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 49.0 - 115 | 49.0 - 115 | Average value: 87.1 Grade Count:101 |
| Hardness, Shore D | 52.0 - 70.0 | 52.0 - 70.0 | Average value: 62.6 Grade Count:12 |
| Tensile Strength, Ultimate | 10.3 - 34.5 MPa | 1500 - 5000 psi | Average value: 22.2 MPa Grade Count:24 |
| Tensile Strength, Yield | 8.96 - 35.2 MPa | 1300 - 5110 psi | Average value: 25.0 MPa Grade Count:190 |
| Film Elongation at Break, MD | 600 - 700 % | 600 - 700 % | Average value: 652 % Grade Count:5 |
| Film Elongation at Break, TD | 570 - 900 % | 570 - 900 % | Average value: 804 % Grade Count:5 |
| Elongation at Break | 2.00 - 600 % | 2.00 - 600 % | Average value: 198 % Grade Count:88 |
| Elongation at Yield | 3.40 - 350 % | 3.40 - 350 % | Average value: 13.9 % Grade Count:93 |
| Modulus of Elasticity | 0.750 - 2.41 GPa | 109 - 350 ksi | Average value: 1.25 GPa Grade Count:24 |
| Flexural Yield Strength | 17.0 - 51.7 MPa | 2470 - 7500 psi | Average value: 29.7 MPa Grade Count:27 |
| Flexural Modulus | 0.172 - 2.89 GPa | 25.0 - 419 ksi | Average value: 1.21 GPa Grade Count:206 |
| Secant Modulus, MD | 0.150 - 0.896 GPa | 21.8 - 130 ksi | Average value: 0.425 GPa Grade Count:5 |
| Secant Modulus, TD | 0.250 - 0.772 GPa | 36.3 - 112 ksi | Average value: 0.447 GPa Grade Count:5 |
| Izod Impact, Notched | 0.267 J/cm - NB | 0.500 ft-lb/in - NB | Average value: 2.19 J/cm Grade Count:161 |
| 0.176 - 7.26104 J/cm @Temperature -30.0 - 4.00 °C | 0.330 - 13.6029 ft-lb/in @Temperature -22.0 - 39.2 °F | Average value: 0.819 J/cm Grade Count:53 | |
| 0.850 - 0.850 J/cm @Temperature -10.0 - 0.000 °C | 1.59 - 1.59 ft-lb/in @Temperature 14.0 - 32.0 °F | Average value: 0.819 J/cm Grade Count:2 | |
| 0.850 - 0.850 J/cm @Thickness 3.17 - 6.40 mm | 1.59 - 1.59 ft-lb/in @Thickness 0.125 - 0.252 in | Average value: 0.819 J/cm Grade Count:2 | |
| 0.250 - 1.35 J/cm @Diameter 0.125 - 3.17 mm | 0.468 - 2.53 ft-lb/in @Diameter 0.00492 - 0.125 in | Average value: 0.819 J/cm Grade Count:11 | |
| 0.250 - 1.35 J/cm @Temperature -20.0 - -20.0 °C | 0.468 - 2.53 ft-lb/in @Temperature -4.00 - -4.00 °F | Average value: 0.819 J/cm Grade Count:11 | |
| Izod Impact, Unnotched | 0.300 J/cm - NB | 0.562 ft-lb/in - NB | Average value: 2.97 J/cm Grade Count:44 |
| 0.200 J/cm - NB @Temperature -30.0 - 0.000 °C | 0.375 ft-lb/in - NB @Temperature -22.0 - 32.0 °F | Average value: 0.535 J/cm Grade Count:27 | |
| Izod Impact, Notched (ISO) | 4.00 - 60.0 kJ/m² | 1.90 - 28.6 ft-lb/in² | Average value: 28.7 kJ/m² Grade Count:11 |
| 3.78 - 13.0 kJ/m² @Temperature -40.0 - -10.0 °C | 1.80 - 6.19 ft-lb/in² @Temperature -40.0 - 14.0 °F | Average value: 6.22 kJ/m² Grade Count:6 | |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² - NB | 6.66 ft-lb/in² - NB | Average value: 19.0 kJ/m² Grade Count:4 |
| Charpy Impact Unnotched | 1000 J/cm² | 4760 ft-lb/in² | Grade Count:8 |
| 5.00 - 999.9 J/cm² @Temperature -20.0 - -20.0 °C | 23.8 - 4759 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 7.00 J/cm² Grade Count:8 | |
| Charpy Impact, Notched | 0.500 - 1000 J/cm² | 2.38 - 4760 ft-lb/in² | Average value: 10.2 J/cm² Grade Count:12 |
| 0.200 - 12.0 J/cm² @Temperature -30.0 - 0.000 °C | 0.952 - 57.1 ft-lb/in² @Temperature -22.0 - 32.0 °F | Average value: 4.35 J/cm² Grade Count:12 | |
| Gardner Impact | 16.3 - 40.7 J | 12.0 - 30.0 ft-lb | Average value: 32.4 J Grade Count:8 |
| 2.26422 - 40.6746 J @Temperature -30.0 - -20.0 °C | 1.67000 - 30.0000 ft-lb @Temperature -22.0 - -4.00 °F | Average value: 24.7 J Grade Count:21 | |
| 19.0945 - 31.8618 J @Temperature -30.0 - -30.0 °C | 14.0834 - 23.5000 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 24.7 J Grade Count:8 | |
| 19.0945 - 31.8618 J @Thickness 3.17 - 3.17 mm | 14.0834 - 23.5000 ft-lb @Thickness 0.125 - 0.125 in | Average value: 24.7 J Grade Count:8 | |
| Falling Dart Impact | 5.09788 - 5.09788 J @Temperature -30.0 - -30.0 °C | 3.76000 - 3.76000 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 5.10 J Grade Count:1 |
| 5.09788 - 5.09788 J @Thickness 1.78 - 1.78 mm | 3.76000 - 3.76000 ft-lb @Thickness 0.0701 - 0.0701 in | Average value: 5.10 J Grade Count:1 | |
| Dart drop Test | 23.2 - 120 g | 0.0512 - 0.265 lb | Average value: 56.8 g Grade Count:3 |
| Film Tensile Strength at Break, MD | 30.0 - 65.0 MPa | 4350 - 9430 psi | Average value: 44.4 MPa Grade Count:5 |
| Film Tensile Strength at Break, TD | 25.0 - 60.0 MPa | 3630 - 8700 psi | Average value: 36.8 MPa Grade Count:5 |
| Tangent Modulus | 740 - 1590 MPa | 107000 - 230000 psi | Average value: 1250 MPa Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.00e+16 ohm-cm | 100 - 1.00e+16 ohm-cm | Average value: 5.17e+15 ohm-cm Grade Count:6 |
| Surface Resistance | 10000 - 1.00e+15 ohm | 10000 - 1.00e+15 ohm | Average value: 1.67e+14 ohm Grade Count:6 |
| Static Decay | 1.00 sec | 1.00 sec | Average value: 1.00 sec Grade Count:3 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 120 - 170 °C | 248 - 338 °F | Average value: 151 °C Grade Count:31 |
| Crystallization Temperature | 110 - 125 °C | 230 - 257 °F | Average value: 120 °C Grade Count:6 |
| Hot Ball Pressure Test | 115 - 125 °C | 239 - 257 °F | Average value: 122 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.4 - 138 °C | 157 - 280 °F | Average value: 97.4 °C Grade Count:171 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 - 115 °C | 100 - 239 °F | Average value: 58.3 °C Grade Count:63 |
| Vicat Softening Point | 55.0 - 155 °C | 131 - 311 °F | Average value: 132 °C Grade Count:68 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:30 |
| Flammability Test | 2.00 - 5.00 | 2.00 - 5.00 | Average value: 3.00 Grade Count:3 |
| Flash Point | 340 °C | 644 °F | Average value: 340 °C Grade Count:8 |
| Oxygen Index | 21.0 - 28.0 % | 21.0 - 28.0 % | Average value: 22.4 % Grade Count:5 |
| Glow Wire Test | 650 °C | 1200 °F | Average value: 650 °C Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.00 - 50.0 % | 4.00 - 50.0 % | Average value: 19.2 % Grade Count:8 |
| Gloss | 3.00 - 94.8 % | 3.00 - 94.8 % | Average value: 47.6 % Grade Count:5 |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 191 - 274 °C | 376 - 525 °F | Average value: 221 °C Grade Count:30 |
| Melt Temperature | 120 - 250 °C | 248 - 482 °F | Average value: 203 °C Grade Count:27 |
| Mold Temperature | 15.0 - 70.0 °C | 59.0 - 158 °F | Average value: 45.1 °C Grade Count:36 |
| Roll Temperature | 50.0 - 60.0 °C | 122 - 140 °F | Average value: 56.7 °C Grade Count:3 |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Average value: 77.8 °C Grade Count:10 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.20 hour Grade Count:5 |
| Moisture Content | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.133 % Grade Count:3 |
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | Average value: 81.8 MPa Grade Count:17 |
| Shelf Life | 12.0 Month | 12.0 Month | Average value: 12.0 Month Grade Count:3 |