- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.77
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 17.6
- 断裂伸长率 [%]: 10.3
- 弯曲强度 [MPa]: 6.21
- 弯曲模量 [MPa]: 1.03
- 硬度: 89.0
- 热变形温度 [℃]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.770 - 1.40 g/cc | 0.0278 - 0.0506 lb/in³ | Average value: 1.08 g/cc Grade Count:30 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 25.0 % Grade Count:6 |
| Water Absorption | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0254 % Grade Count:13 |
| Linear Mold Shrinkage | 0.00800 - 0.0226 cm/cm | 0.00800 - 0.0226 in/in | Average value: 0.0135 cm/cm Grade Count:26 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0130 - 0.0200 cm/cm | 0.0130 - 0.0200 in/in | Average value: 0.0168 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.00900 - 0.0210 cm/cm | 0.00900 - 0.0210 in/in | Average value: 0.0153 cm/cm Grade Count:8 |
| Melt Flow | 3.00 - 25.0 g/10 min | 3.00 - 25.0 g/10 min | Average value: 9.59 g/10 min Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 89.0 - 100 | 89.0 - 100 | Average value: 96.2 Grade Count:10 |
| Tensile Strength, Ultimate | 6.21 - 37.0 MPa | 900 - 5370 psi | Average value: 24.0 MPa Grade Count:22 |
| Tensile Strength, Yield | 17.6 - 26.2 MPa | 2550 - 3800 psi | Average value: 21.3 MPa Grade Count:9 |
| Elongation at Break | 2.00 - 100 % | 2.00 - 100 % | Average value: 22.3 % Grade Count:23 |
| Elongation at Yield | 6.30 - 100 % | 6.30 - 100 % | Average value: 21.5 % Grade Count:7 |
| Modulus of Elasticity | 1.32 - 3.25 GPa | 191 - 471 ksi | Average value: 2.08 GPa Grade Count:22 |
| Flexural Yield Strength | 10.3 - 55.0 MPa | 1500 - 7980 psi | Average value: 35.3 MPa Grade Count:25 |
| Flexural Modulus | 1.03 - 3.10 GPa | 149 - 450 ksi | Average value: 1.90 GPa Grade Count:28 |
| Compressive Yield Strength | 29.0 - 34.5 MPa | 4200 - 5000 psi | Average value: 32.1 MPa Grade Count:4 |
| Izod Impact, Notched | 0.160 - 1.60 J/cm | 0.300 - 3.00 ft-lb/in | Average value: 0.404 J/cm Grade Count:21 |
| Izod Impact, Unnotched | 0.300 - 10.7 J/cm | 0.562 - 20.0 ft-lb/in | Average value: 4.14 J/cm Grade Count:14 |
| 0.200 - 0.200 J/cm @Temperature 0.000 - 0.000 °C | 0.375 - 0.375 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.200 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 2.70 - 6.00 kJ/m² | 1.28 - 2.86 ft-lb/in² | Average value: 3.90 kJ/m² Grade Count:3 |
| 4.00 - 4.00 kJ/m² @Temperature -30.0 - -30.0 °C | 1.90 - 1.90 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 4.00 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 1.50 - 4.50 J/cm² | 7.14 - 21.4 ft-lb/in² | Average value: 3.37 J/cm² Grade Count:7 |
| 1.80 - 3.40 J/cm² @Temperature -20.0 - -20.0 °C | 8.57 - 16.2 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 2.44 J/cm² Grade Count:5 | |
| Charpy Impact, Notched | 0.300 - 0.600 J/cm² | 1.43 - 2.86 ft-lb/in² | Average value: 0.467 J/cm² Grade Count:6 |
| 0.200 - 0.500 J/cm² @Temperature -20.0 - -20.0 °C | 0.952 - 2.38 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 0.340 J/cm² Grade Count:5 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+17 ohm-cm | 1.00e+12 - 1.00e+17 ohm-cm | Average value: 1.47e+16 ohm-cm Grade Count:13 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Average value: 19.7 kV/mm Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 37.8 - 68.0 µm/m-°C | 21.0 - 37.8 µin/in-°F | Average value: 58.4 µm/m-°C Grade Count:9 |
| Melting Point | 150 - 170 °C | 302 - 338 °F | Average value: 164 °C Grade Count:14 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 - 125 °C | 190 - 257 °F | Average value: 115 °C Grade Count:13 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 - 160 °C | 133 - 320 °F | Average value: 78.5 °C Grade Count:26 |
| Vicat Softening Point | 94.0 - 156 °C | 201 - 313 °F | Average value: 111 °C Grade Count:9 |
| Flammability, UL94 | HB | HB | Grade Count:16 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 240 °C | 380 - 464 °F | Average value: 211 °C Grade Count:7 |
| Melt Temperature | 191 - 250 °C | 375 - 482 °F | Average value: 221 °C Grade Count:15 |
| Mold Temperature | 20.0 - 80.0 °C | 68.0 - 176 °F | Average value: 51.0 °C Grade Count:22 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 80.9 °C Grade Count:10 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 2.50 hour Grade Count:10 |
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | Average value: 87.9 MPa Grade Count:18 |