- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.098
- 缺口冲击强度: 5.98
- 拉伸强度 [MPa]: 15.9
- 弯曲模量 [MPa]: 1.00
- 硬度: 50.0
- 热变形温度 [℃]: 73.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.098 g/cc | 0.03967 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 50 | 50 | ASTM D785 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
| Flexural Strength | 17.0 MPa | 2470 psi | ASTM D790 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 5.98 J/cm | 11.2 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | |