- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.96
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 33.0
- 弯曲模量 [MPa]: 1.60
- 硬度: 91.0
- 热变形温度 [℃]: 97.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 9.8 % | 9.8 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 91 | 91 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Tensile Modulus | 1.300 GPa | 188.5 ksi | ASTM D638 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.750 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | |