- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 16.0
- 弯曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Filler Content | 50 % | 50 % | ISO 3451 / 1 |
| Melt Index of Compound | 10 g/10 min @Load 2.16 kg, Temperature 230 °C | 10 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ISO 868 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75 |
| Vicat Softening Point | 78.0 °C | 172 °F | 49 N; ISO 306 |