- 密度 [g/cm3]: 1.23
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 1.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Filler Content | 40 % | 40 % | ISO 3451 / 1 |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 50 % | 50 % | ISO 527 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Vicat Softening Point | 76.0 °C | 169 °F | 49 N; ISO 306 |