- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 0.91
- 弯曲强度 [MPa]: 95.0
- 弯曲模量 [MPa]: 7.00
- 硬度: 108.0
- 热变形温度 [℃]: 163.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Ultimate | 95.0 MPa | 13800 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 225 °C | 437 °F | Approximate middle barrel temperature. |