- 密度 [g/cm3]: 1.01
- 弯曲强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 2.20
- 硬度: 109.0
- 热变形温度 [℃]: 129.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Unnotched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 100 ohm-cm | 10.0 - 100 ohm-cm | |
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |