- 熔体流动速率 [g/10min]: 0.7
- 缺口冲击强度: 1.98
- 弯曲模量 [MPa]: 4.486
- 硬度: 104.0
- 热变形温度 [℃]: 153.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 4.486 GPa | 650.6 ksi | ASTM D790 |
| Izod Impact, Notched | 1.98 J/cm | 3.71 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | ASTM D648 |