- 熔体流动速率 [g/10min]: 5.0
- 缺口冲击强度: 0.72
- 拉伸强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 4.48
- 硬度: 115.0
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 5.0 g/10 min @Temperature 230 °C | 5.0 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.720 J/cm | 1.35 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.85 J/cm | 3.47 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |