- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 0.64
- 拉伸强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 1.93
- 硬度: 89.0
- 热变形温度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 89 | 89 | ASTM D785 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D648 |