- 熔体流动速率 [g/10min]: 20.0
- 缺口冲击强度: 0.267
- 弯曲模量 [MPa]: 1.31
- 热变形温度 [℃]: 102.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Temperature 230 °C | 20 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 31.7 MPa | 4600 psi | at max load; ASTM D638 |
| Elongation at Break | 10 % | 10 % | at max load; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |