- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 34.5
- 弯曲模量 [MPa]: 1.31
- 硬度: 95.0
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | at break; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | 50 mm/min span, 5 mm/min, 1 % secant; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 °C | 320 °F | |