- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 2.0
- 弯曲强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 0.900
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 48 hr, at 80 and 121°C; ASTM D955 | ||
| 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 72 hr; ASTM D955 | |||
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | 48 hr at 121°C; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 65 | 65 | 15 sec delay; ASTM D2240 | ||
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | at max load; ASTM D638 | ||
| Elongation at Break | 30 % | 30 % | ASTM D412 | ||
| Flexural Modulus | 0.900 GPa | 131 ksi | at 70°C, tangent | ||
| 1.40 GPa | 203 ksi | tangent; ASTM D790 | |||
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ASTM D256 | ||
| Falling Dart Impact | 6.01 J | 4.43 ft-lb | at -30°C; ASTM D3029 | ||
| Tear Strength | 110 kN/m | 628 pli | ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 15.0 µin/in-°F @Temperature -22.0 - 86.0 °F | 2.7 mm/mm; ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C @Thickness 3.20 mm | 194 °F @Thickness 0.126 in | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 °C | 428 °F | by DSC, 10°C per 220 minutes | ||
| Descriptive Properties | |||||
| Heat Sag | 15 mm | ASTM D3769, 1 hr, at 121°C | |||