- 成型收缩率 [%]: 0.004
- 缺口冲击强度: 0.17
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 2.30
- 硬度: 115.0
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | 48 hr at 80°C; ASTM D955 |
| 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | 72 hr; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Hardness, Shore D | 75 | 75 | 15 sec delay; ASTM D2240 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | at max load; ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 2.30 GPa | 334 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 0.170 J/cm | 0.318 ft-lb/in | ASTM D256 |
| 0.0400 J/cm @Temperature -40.0 °C | 0.0749 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| 0.0500 J/cm @Temperature 0.000 °C | 0.0937 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C @Thickness 3.20 mm | 185 °F @Thickness 0.126 in | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 3.20 mm | 167 °F @Thickness 0.126 in | ASTM D648 |