- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 4.2
- 弯曲强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 0.690
- 热变形温度 [℃]: 77.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 48 hr at 80°C; ASTM D955 | ||
| 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | 72 hr; ASTM D955 | |||
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | 48 hr at 121°C; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 55 | 55 | 15 sec delay; ASTM D2240 | ||
| Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 | ||
| Elongation at Break | 30 % | 30 % | ASTM D412 | ||
| Flexural Modulus | 0.690 GPa | 100 ksi | tangent; ASTM D790 | ||
| Izod Impact, Notched | 4.20 J/cm | 7.87 ft-lb/in | ASTM D256 | ||
| Tear Strength | 100 kN/m | 571 pli | ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 15.0 µin/in-°F @Temperature -22.0 - 86.0 °F | 3.45 mm/mm; ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C @Thickness 3.20 mm | 171 °F @Thickness 0.126 in | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 °C | 410 °F | by DSC, 10°C per 210 minutes | ||
| Descriptive Properties | |||||
| Heat Sag | 30 mm | ASTM D3769, 1 hr at 80°C | |||