- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 1.0
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1.00
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Gardner Impact | 10.8 J @Temperature -30.0 °C | 7.97 ft-lb @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability Test | <= 102 | <= 102 | mm/min |