- 密度 [g/cm3]: 0.905
- 缺口冲击强度: 0.374
- 拉伸强度 [MPa]: 36.9
- 弯曲模量 [MPa]: 1.59
- 硬度: 97.0
- 热变形温度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 3.8 g/10 min @Temperature 230 °C | 3.8 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Hardness, Shore D | 71 | 71 | ASTM D2240 |
| Tensile Strength, Yield | 36.9 MPa | 5350 psi | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.59 GPa | 230 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C | 0.700 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |