- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 0.374
- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 1.07
- 硬度: 80.0
- 热变形温度 [℃]: 79.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | 0.5 in/min, Tangent Method; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature -30.0 °C | 0.700 ft-lb/in @Temperature -22.0 °F | ASTM D256 |
| 0.801 J/cm @Temperature 0.000 °C | 1.50 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |
| NB @Temperature 22.8 °C | NB @Temperature 73.0 °F | ASTM D256 | |
| Falling Dart Impact | 28.2 J @Temperature -30.0 °C | 20.8 ft-lb @Temperature -22.0 °F | 0.5" Tup, 150"/sec; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.4 °C | 175 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.3 °C | 110 °F | ASTM D648 |