- 熔体流动速率 [g/10min]: 19.0
- 密度 [g/cm3]: 0.905
- 拉伸强度 [MPa]: 29.5
- 硬度: 93.0
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 230 °C | 19 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 93 | 93 | ISO 2039-2 |
| Tensile Strength, Yield | 29.5 MPa | 4280 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 11 % | 11 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.25 GPa | 181 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 30.0 - 40.0 °C | 86.0 - 104 °F | |