- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.902
- 拉伸强度 [MPa]: 40.0
- 硬度: 112.0
- 热变形温度 [℃]: 122.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 | 112 | ISO 2039-2 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |