- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.94
- 缺口冲击强度: 33.0
- 拉伸强度 [MPa]: 15.7
- 弯曲模量 [MPa]: 0.930
- 热变形温度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0105 cm/cm | 0.0105 in/in | Borealis Method |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C | 11 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 50 g/10 min @Load 5.00 kg, Temperature 230 °C | 50 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 28.0 MPa | 4060 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 15.70 MPa | 2277 psi | At 50 mm/min; ISO 527-2 |
| Flexural Modulus | 0.930 GPa | 135 ksi | At 1 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU |
| Charpy Impact, Notched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |
| 0.600 J/cm² @Temperature -20.0 °C | 2.86 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 41.7 µin/in-°F @Temperature 73.4 - 176 °F | Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | ISO 75-2 |
| Vicat Softening Point | 43.0 °C | 109 °F | B (50N); ISO 306 |
| 118 °C | 244 °F | A (10N); ISO 306 | |
| Shrinkage | 0.15 % | 0.15 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |