- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.04
- 缺口冲击强度: 32.0
- 拉伸强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 1.25
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Borealis Method |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C | 25 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133/12 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 15.00 MPa | 2176 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 |
| Flexural Modulus | 1.25 GPa | 181 ksi | At 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | ISO 180/1A |
| 4.50 kJ/m² @Temperature -20.0 °C | 2.14 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² @Temperature -20.0 °C | 2.38 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-2 |
| Shrinkage | 0.10 % | 0.10 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |