Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled

Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled 物性表: Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled物性表及特性介绍,Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled注塑参数详情,如需Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.39
  • 吸水率 [%]: 0.02
  • 缺口冲击强度: 0.534
  • 断裂伸长率 [%]: 130
  • 弯曲强度 [MPa]: 20.8
  • 弯曲模量 [MPa]: 7.20
  • 热变形温度 [℃]: 270.0
 
Physical PropertiesMetricEnglishComments
Density 1.39 - 1.78 g/cc0.0502 - 0.0643 lb/in³Average value: 1.70 g/cc Grade Count:34
Filler Content 40.0 %40.0 %Average value: 40.0 % Grade Count:8
Water Absorption 0.0200 - 0.100 %0.0200 - 0.100 %Average value: 0.0450 % Grade Count:6
Moisture Absorption at Equilibrium 0.0100 - 0.0400 %0.0100 - 0.0400 %Average value: 0.0233 % Grade Count:3
Linear Mold Shrinkage 0.000 - 0.00400 cm/cm0.000 - 0.00400 in/inAverage value: 0.00156 cm/cm Grade Count:28
Linear Mold Shrinkage, Transverse 0.00200 - 0.0120 cm/cm0.00200 - 0.0120 in/inAverage value: 0.00545 cm/cm Grade Count:25
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 44.0 - 96.044.0 - 96.0Average value: 68.0 Grade Count:6
Tensile Strength, Ultimate 20.8 - 177 MPa3020 - 25700 psiAverage value: 116 MPa Grade Count:35
 9.28 - 138 MPa
@Temperature -20.0 - 200 °C
1350 - 20000 psi
@Temperature -4.00 - 392 °F
Average value: 49.7 MPa Grade Count:1
 9.28 - 138 MPa
@Strain 0.230 - 4.21 %
1350 - 20000 psi
@Strain 0.230 - 4.21 %
Average value: 49.7 MPa Grade Count:1
Elongation at Break 0.500 - 3.50 %0.500 - 3.50 %Average value: 1.66 % Grade Count:35
Modulus of Elasticity 8.50 - 34.5 GPa1230 - 5000 ksiAverage value: 16.1 GPa Grade Count:34
Flexural Yield Strength 130 - 250 MPa18900 - 36300 psiAverage value: 192 MPa Grade Count:35
Flexural Modulus 7.20 - 27.6 GPa1040 - 4000 ksiAverage value: 15.0 GPa Grade Count:35
Compressive Yield Strength 53.0 - 134 MPa7690 - 19400 psiAverage value: 110 MPa Grade Count:5
Compressive Modulus 7.70 - 18.0 GPa1120 - 2610 ksiAverage value: 14.2 GPa Grade Count:5
Izod Impact, Notched 0.534 - 1.12 J/cm1.00 - 2.10 ft-lb/inAverage value: 0.798 J/cm Grade Count:6
Izod Impact, Unnotched 2.67 - 4.27 J/cm5.00 - 8.00 ft-lb/inAverage value: 3.38 J/cm Grade Count:3
Izod Impact, Notched (ISO) 4.00 - 30.0 kJ/m²1.90 - 14.3 ft-lb/in²Average value: 12.0 kJ/m² Grade Count:17
Izod Impact, Unnotched (ISO) 14.0 - 45.0 kJ/m²6.66 - 21.4 ft-lb/in²Average value: 26.8 kJ/m² Grade Count:11
 20.0 - 20.0 kJ/m²
@Temperature -30.0 - -30.0 °C
9.52 - 9.52 ft-lb/in²
@Temperature -22.0 - -22.0 °F
Average value: 20.0 kJ/m² Grade Count:2
Charpy Impact Unnotched 2.00 - 5.40 J/cm²9.52 - 25.7 ft-lb/in²Average value: 3.05 J/cm² Grade Count:14
 1.80 - 4.00 J/cm²
@Temperature -30.0 - 30.0 °C
8.57 - 19.0 ft-lb/in²
@Temperature -22.0 - 86.0 °F
Average value: 2.45 J/cm² Grade Count:4
Charpy Impact, Notched 0.500 - 2.70 J/cm²2.38 - 12.8 ft-lb/in²Average value: 1.20 J/cm² Grade Count:24
 0.600 - 1.50 J/cm²
@Temperature -30.0 - 30.0 °C
2.86 - 7.14 ft-lb/in²
@Temperature -22.0 - 86.0 °F
Average value: 1.27 J/cm² Grade Count:4
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 100000 - 1.00e+17 ohm-cm100000 - 1.00e+17 ohm-cmAverage value: 9.12e+15 ohm-cm Grade Count:19
Surface Resistance 1.00e+7 - 1.00e+17 ohm1.00e+7 - 1.00e+17 ohmAverage value: 2.49e+16 ohm Grade Count:21
Dielectric Constant 3.50 - 4.403.50 - 4.40Average value: 3.91 Grade Count:15
Dielectric Strength 22.6 - 59.0 kV/mm575 - 1500 kV/inAverage value: 34.3 kV/mm Grade Count:12
Dissipation Factor 0.00200 - 0.02800.00200 - 0.0280Average value: 0.0127 Grade Count:15
Arc Resistance 140 - 180 sec140 - 180 secAverage value: 163 sec Grade Count:4
Comparative Tracking Index 150 - 249 V150 - 249 VAverage value: 181 V Grade Count:15
 
Thermal PropertiesMetricEnglishComments
CTE, linear 1.00 - 17.0 µm/m-°C0.556 - 9.44 µin/in-°FAverage value: 5.13 µm/m-°C Grade Count:25
 -2.00 - 3.00 µm/m-°C
@Temperature 55.0 - 320 °C
-1.11 - 1.67 µin/in-°F
@Temperature 131 - 608 °F
Average value: 1.79 µm/m-°C Grade Count:2
 -2.00 - 5.00 µm/m-°C
@Temperature 55.0 - 320 °C
-1.11 - 2.78 µin/in-°F
@Temperature 131 - 608 °F
Average value: 1.79 µm/m-°C Grade Count:4
 -2.00 - 5.00 µm/m-°C
@Thickness 2.00 - 4.00 mm
-1.11 - 2.78 µin/in-°F
@Thickness 0.0787 - 0.157 in
Average value: 1.79 µm/m-°C Grade Count:4
CTE, linear, Transverse to Flow 18.0 - 82.0 µm/m-°C10.0 - 45.6 µin/in-°FAverage value: 55.7 µm/m-°C Grade Count:25
 71.0 - 88.0 µm/m-°C
@Temperature 55.0 - 320 °C
39.4 - 48.9 µin/in-°F
@Temperature 131 - 608 °F
Average value: 84.1 µm/m-°C Grade Count:2
 71.0 - 94.0 µm/m-°C
@Temperature 55.0 - 320 °C
39.4 - 52.2 µin/in-°F
@Temperature 131 - 608 °F
Average value: 84.1 µm/m-°C Grade Count:4
 71.0 - 94.0 µm/m-°C
@Thickness 2.00 - 4.00 mm
39.4 - 52.2 µin/in-°F
@Thickness 0.0787 - 0.157 in
Average value: 84.1 µm/m-°C Grade Count:4
Melting Point 280 - 352 °C536 - 666 °FAverage value: 329 °C Grade Count:26
Deflection Temperature at 0.46 MPa (66 psi) 270 - 286 °C518 - 547 °FAverage value: 280 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi) 217 - 356 °C423 - 673 °FAverage value: 273 °C Grade Count:35
Deflection Temperature at 8.0 MPa 130 - 267 °C266 - 513 °FAverage value: 206 °C Grade Count:5
Vicat Softening Point 176 - 224 °C349 - 435 °FAverage value: 198 °C Grade Count:5
UL RTI, Electrical 130 - 240 °C266 - 464 °FAverage value: 191 °C Grade Count:5
UL RTI, Mechanical with Impact 130 - 220 °C266 - 428 °FAverage value: 180 °C Grade Count:5
UL RTI, Mechanical without Impact 130 - 240 °C266 - 464 °FAverage value: 199 °C Grade Count:4
Flammability, UL94 V-0V-0Grade Count:24
 
Processing PropertiesMetricEnglishComments
Processing Temperature 20.0 - 391 °C68.0 - 735 °FAverage value: 91.7 °C Grade Count:22
Feed Temperature 40.0 - 80.0 °C104 - 176 °FAverage value: 66.4 °C Grade Count:11
Die Temperature 300 - 380 °C572 - 716 °FAverage value: 341 °C Grade Count:16
Melt Temperature 271 - 385 °C520 - 725 °FAverage value: 337 °C Grade Count:31
Mold Temperature 30.0 - 160 °C86.0 - 320 °FAverage value: 90.7 °C Grade Count:16
Drying Temperature 135 - 170 °C275 - 338 °FAverage value: 153 °C Grade Count:28
Dry Time 3.00 - 24.0 hour3.00 - 24.0 hourAverage value: 5.85 hour Grade Count:27
Moisture Content 0.0100 %0.0100 %Average value: 0.0100 % Grade Count:25
Dew Point -40.0 - -28.9 °C-40.0 - -20.0 °FAverage value: -39.1 °C Grade Count:11
Injection Pressure 34.5 - 150 MPa5000 - 21800 psiAverage value: 95.4 MPa Grade Count:20
Hold Pressure 50.0 - 150 MPa7250 - 21800 psiAverage value: 100 MPa Grade Count:13
Back Pressure 3.00 - 3.00 MPa435 - 435 psiAverage value: 3.00 MPa Grade Count:10
Screw Speed 80.0 - 200 rpm80.0 - 200 rpmAverage value: 142 rpm Grade Count:14
Hot-Working Temperature 300 - 370 °C572 - 698 °FAverage value: 339 °C Grade Count:9

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31753.html

免责声明: 本文 Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4