- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.588
- 断裂伸长率 [%]: 158
- 弯曲强度 [MPa]: 88.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.89 g/cc | 0.0524 - 0.0683 lb/in³ | Average value: 1.74 g/cc Grade Count:14 |
| Filler Content | 45.0 % | 45.0 % | Average value: 45.0 % Grade Count:5 |
| Water Absorption | 0.0100 - 0.100 % | 0.0100 - 0.100 % | Average value: 0.0700 % Grade Count:3 |
| Moisture Absorption at Equilibrium | 0.00600 - 1.10 % | 0.00600 - 1.10 % | Average value: 0.372 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000100 - 0.00200 cm/cm | 0.000100 - 0.00200 in/in | Average value: 0.000927 cm/cm Grade Count:11 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.00500 cm/cm | 0.00100 - 0.00500 in/in | Average value: 0.00425 cm/cm Grade Count:12 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 58.0 - 93.0 | 58.0 - 93.0 | Average value: 72.3 Grade Count:3 |
| Tensile Strength, Ultimate | 88.0 - 160 MPa | 12800 - 23200 psi | Average value: 124 MPa Grade Count:14 |
| 20.0 - 190 MPa @Temperature -40.0 - 250 °C | 2900 - 27600 psi @Temperature -40.0 - 482 °F | Average value: 85.1 MPa Grade Count:3 | |
| 20.0 - 190 MPa @Thickness 1.00 - 4.00 mm | 2900 - 27600 psi @Thickness 0.0394 - 0.157 in | Average value: 85.1 MPa Grade Count:3 | |
| Elongation at Break | 0.600 - 3.30 % | 0.600 - 3.30 % | Average value: 1.46 % Grade Count:14 |
| 0.300 - 0.900 % @Temperature -40.0 - 250 °C | 0.300 - 0.900 % @Temperature -40.0 - 482 °F | Average value: 0.633 % Grade Count:2 | |
| 0.300 - 0.900 % @Thickness 1.00 - 4.00 mm | 0.300 - 0.900 % @Thickness 0.0394 - 0.157 in | Average value: 0.633 % Grade Count:2 | |
| Modulus of Elasticity | 12.0 - 24.5 GPa | 1740 - 3550 ksi | Average value: 18.5 GPa Grade Count:13 |
| 6.00 - 27.0 GPa @Temperature -40.0 - 250 °C | 870 - 3920 ksi @Temperature -40.0 - 482 °F | Average value: 15.6 GPa Grade Count:3 | |
| 6.00 - 27.0 GPa @Thickness 1.00 - 4.00 mm | 870 - 3920 ksi @Thickness 0.0394 - 0.157 in | Average value: 15.6 GPa Grade Count:3 | |
| Flexural Yield Strength | 158 - 250 MPa | 22900 - 36300 psi | Average value: 192 MPa Grade Count:14 |
| 10.0 - 300 MPa @Temperature -40.0 - 250 °C | 1450 - 43500 psi @Temperature -40.0 - 482 °F | Average value: 121 MPa Grade Count:3 | |
| 10.0 - 300 MPa @Thickness 0.790 - 4.00 mm | 1450 - 43500 psi @Thickness 0.0311 - 0.157 in | Average value: 121 MPa Grade Count:3 | |
| Flexural Modulus | 10.0 - 24.0 GPa | 1450 - 3480 ksi | Average value: 16.8 GPa Grade Count:14 |
| 5.00 - 25.5 GPa @Temperature -40.0 - 250 °C | 725 - 3700 ksi @Temperature -40.0 - 482 °F | Average value: 13.8 GPa Grade Count:3 | |
| 5.00 - 25.5 GPa @Thickness 0.790 - 4.00 mm | 725 - 3700 ksi @Thickness 0.0311 - 0.157 in | Average value: 13.8 GPa Grade Count:3 | |
| Compressive Yield Strength | 21.3 - 152 MPa | 3090 - 22000 psi | Average value: 88.4 MPa Grade Count:5 |
| Compressive Modulus | 18.0 - 21.0 GPa | 2610 - 3050 ksi | Average value: 19.8 GPa Grade Count:3 |
| Izod Impact, Notched | 0.588 - 2.50 J/cm | 1.10 - 4.68 ft-lb/in | Average value: 1.38 J/cm Grade Count:5 |
| Izod Impact, Unnotched | 3.16 - 6.53 J/cm | 5.92 - 12.2 ft-lb/in | Average value: 4.80 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 8.00 - 12.0 kJ/m² | 3.81 - 5.71 ft-lb/in² | Average value: 10.0 kJ/m² Grade Count:6 |
| Charpy Impact Unnotched | 1.00 - 1.90 J/cm² | 4.76 - 9.04 ft-lb/in² | Average value: 1.61 J/cm² Grade Count:7 |
| 1.20 - 1.30 J/cm² @Temperature -30.0 - -30.0 °C | 5.71 - 6.19 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.27 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.360 - 1.20 J/cm² | 1.71 - 5.71 ft-lb/in² | Average value: 0.866 J/cm² Grade Count:10 |
| 0.800 - 1.00 J/cm² @Temperature -30.0 - -30.0 °C | 3.81 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.950 J/cm² Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+16 ohm-cm | 1.00e+12 - 1.00e+16 ohm-cm | Average value: 2.42e+15 ohm-cm Grade Count:11 |
| Surface Resistance | 1.00e+11 - 1.00e+17 ohm | 1.00e+11 - 1.00e+17 ohm | Average value: 9.84e+15 ohm Grade Count:11 |
| Dielectric Constant | 3.40 - 5.00 | 3.40 - 5.00 | Average value: 4.32 Grade Count:12 |
| 5.20 - 5.60 @Temperature 120 - 200 °C | 5.20 - 5.60 @Temperature 248 - 392 °F | Average value: 5.37 Grade Count:2 | |
| 5.20 - 5.60 @Frequency 60.0 - 1.00e+6 Hz | 5.20 - 5.60 @Frequency 60.0 - 1.00e+6 Hz | Average value: 5.37 Grade Count:2 | |
| Dielectric Strength | 21.0 - 45.0 kV/mm | 533 - 1140 kV/in | Average value: 30.4 kV/mm Grade Count:10 |
| 20.0 - 40.0 kV/mm @Temperature 100 - 200 °C | 508 - 1020 kV/in @Temperature 212 - 392 °F | Average value: 27.6 kV/mm Grade Count:3 | |
| 20.0 - 40.0 kV/mm @Thickness 0.800 - 3.20 mm | 508 - 1020 kV/in @Thickness 0.0315 - 0.126 in | Average value: 27.6 kV/mm Grade Count:3 | |
| Dissipation Factor | 0.00600 - 0.0310 | 0.00600 - 0.0310 | Average value: 0.0171 Grade Count:12 |
| 0.00800 - 0.0830 @Temperature 120 - 200 °C | 0.00800 - 0.0830 @Temperature 248 - 392 °F | Average value: 0.0226 Grade Count:2 | |
| 0.00800 - 0.0830 @Frequency 60.0 - 1.00e+6 Hz | 0.00800 - 0.0830 @Frequency 60.0 - 1.00e+6 Hz | Average value: 0.0226 Grade Count:2 | |
| Comparative Tracking Index | 150 - 250 V | 150 - 250 V | Average value: 186 V Grade Count:10 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 2.00 - 15.0 µm/m-°C | 1.11 - 8.33 µin/in-°F | Average value: 4.82 µm/m-°C Grade Count:12 |
| -1.00 - 7.00 µm/m-°C @Temperature 55.0 - 260 °C | -0.556 - 3.89 µin/in-°F @Temperature 131 - 500 °F | Average value: 2.88 µm/m-°C Grade Count:4 | |
| -1.00 - 7.00 µm/m-°C @Thickness 2.00 - 4.00 mm | -0.556 - 3.89 µin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 2.88 µm/m-°C Grade Count:4 | |
| CTE, linear, Transverse to Flow | 17.0 - 80.0 µm/m-°C | 9.44 - 44.4 µin/in-°F | Average value: 55.4 µm/m-°C Grade Count:12 |
| 76.0 - 100 µm/m-°C @Temperature 55.0 - 260 °C | 42.2 - 55.6 µin/in-°F @Temperature 131 - 500 °F | Average value: 83.8 µm/m-°C Grade Count:4 | |
| 76.0 - 100 µm/m-°C @Thickness 2.00 - 4.00 mm | 42.2 - 55.6 µin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 83.8 µm/m-°C Grade Count:4 | |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Average value: 1.50 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.320 - 0.400 W/m-K | 2.22 - 2.78 BTU-in/hr-ft²-°F | Average value: 0.357 W/m-K Grade Count:3 |
| Melting Point | 280 - 357 °C | 536 - 675 °F | Average value: 337 °C Grade Count:13 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 - 315 °C | 464 - 599 °F | Average value: 286 °C Grade Count:14 |
| Deflection Temperature at 8.0 MPa | 203 - 271 °C | 397 - 520 °F | Average value: 233 °C Grade Count:3 |
| UL RTI, Electrical | 130 - 240 °C | 266 - 464 °F | Average value: 210 °C Grade Count:5 |
| UL RTI, Mechanical with Impact | 130 - 210 °C | 266 - 410 °F | Average value: 189 °C Grade Count:5 |
| UL RTI, Mechanical without Impact | 130 - 240 °C | 266 - 464 °F | Average value: 209 °C Grade Count:4 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:13 |
| Oxygen Index | 33.0 - 45.0 % | 33.0 - 45.0 % | Average value: 40.2 % Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 275 °C | 68.0 - 527 °F | Average value: 99.4 °C Grade Count:7 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 58.6 °C Grade Count:7 |
| Die Temperature | 290 - 370 °C | 554 - 698 °F | Average value: 344 °C Grade Count:7 |
| Melt Temperature | 270 - 375 °C | 518 - 707 °F | Average value: 342 °C Grade Count:13 |
| Mold Temperature | 30.0 - 160 °C | 86.0 - 320 °F | Average value: 87.1 °C Grade Count:11 |
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | Average value: 151 °C Grade Count:12 |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | Average value: 3.67 hour Grade Count:12 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:11 |
| Dew Point | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:3 |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | Average value: 100 MPa Grade Count:7 |
| Hold Pressure | 48.0 - 150 MPa | 6960 - 21800 psi | Average value: 90.8 MPa Grade Count:7 |
| Back Pressure | 3.00 MPa | 435 psi | Average value: 3.00 MPa Grade Count:7 |
| Hot-Working Temperature | 285 - 370 °C | 545 - 698 °F | Average value: 331 °C Grade Count:3 |