- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 14.0
- 弯曲模量 [MPa]: 9.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | at 50% RH; ISO 62 |
| Moisture Vapor Transmission | 0.0157 cc-mm/m²-24hr-atm | 0.0400 cc-mil/100 in²-24hr-atm | at 38°C; DIN 53122-2 |
| Oxygen Transmission | 0.0394 cc-mm/m²-24hr-atm | 0.100 cc-mil/100 in²-24hr-atm | 73°F, 100%RH; DIN 53380 part 3 |
| 0.0472 cc-mm/m²-24hr-atm | 0.120 cc-mil/100 in²-24hr-atm | 73°F, 0% RH; DIN 53380 part 3 | |
| Carbon Dioxide Transmission | 0.0945 cc-mm/m²-24hr-atm | 0.240 cc-mil/100 in²-24hr-atm | 25°C, 100% RH; ISO/CD 15105-2C |
| Melt Flow | 18 g/10 min @Temperature 230 °C | 18 g/10 min @Temperature 446 °F | I2, nominal |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 153 MPa | 22200 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 2.4 % | 2.4 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.5 GPa | 1670 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 178 MPa | 25800 psi | ISO 178 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 110 °C | 230 °F | ISO 3146 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 185 - 195 °C | 365 - 383 °F | |
| Middle Barrel Temperature | 205 - 215 °C | 401 - 419 °F | |
| Front Barrel Temperature | 225 - 235 °C | 437 - 455 °F | |
| Die Temperature | 225 - 235 °C | 437 - 455 °F | |
| Melt Temperature | 225 - 235 °C | 437 - 455 °F | |