- 密度 [g/cm3]: 2.02
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.02 g/cc | 0.0730 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Flexural Strength | 180 MPa | 26100 psi | Flexural Strain: 2.2%; ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz | 7.0 @Frequency 1e+6 Hz | Volumetric method |
| Dissipation Factor | 0.0020 @Frequency 3.00e+9 Hz | 0.0020 @Frequency 3.00e+9 Hz | Perturbation method by cavity resonator |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C | 5.56 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |