- 缺口冲击强度: 0.368
- 断裂伸长率 [%]: 73.02
- 弯曲强度 [MPa]: 47.78
- 弯曲模量 [MPa]: 2.12
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 1500 | 1500 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 87 | 87 | |||
| Tensile Strength, Ultimate | 47.78 MPa | 6930 psi | |||
| Elongation at Break | 14.4 % | 14.4 % | |||
| Flexural Yield Strength | 73.02 MPa | 10590 psi | |||
| Flexural Modulus | 2.12 GPa | 307 ksi | |||
| Compressive Yield Strength | 68.95 MPa | 10000 psi | |||
| Compressive Modulus | 2.21 GPa | 321 ksi | |||
| Izod Impact, Notched | 0.368 J/cm | 0.689 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 7.52e+14 ohm-cm | 7.52e+14 ohm-cm | |||
| Surface Resistance | 4.71e+14 ohm | 4.71e+14 ohm | |||
| Dielectric Constant | 3.13 @Frequency 1e+6 Hz | 3.13 @Frequency 1e+6 Hz | |||
| 3.4 @Frequency 1000 Hz | 3.4 @Frequency 1000 Hz | ||||
| 3.46 @Frequency 60 Hz | 3.46 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0044 @Frequency 60 Hz | 0.0044 @Frequency 60 Hz | |||
| 0.012 @Frequency 1000 Hz | 0.012 @Frequency 1000 Hz | ||||
| 0.024 @Frequency 1e+6 Hz | 0.024 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 62.0 °C | 144 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 360 min | 360 min | 500 g at 360°C | ||
| Descriptive Properties | |||||
| Exotherm | 130°C | Peak | |||