| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.90 g/cc | 1.90 g/cc | |||
| Mechanical Properties | Metric | English | Comments | ||
| Shear Strength | 9.480 MPa | 1375 psi | Strength can be increased 40-50% by heat curing; ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |||
| Dielectric Strength | 9.84 kV/mm | 250 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 33.7 µm/m-°C @Temperature 20.0 °C | 18.7 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 1.22 W/m-K | 8.50 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | at 200°F (Recommended Cure) | ||
| 1440 - 2880 min | 24.0 - 48.0 hour | Room Temperature (Alternate Cure) | |||
| Pot Life | 240 min | 240 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Excellent | ||||
| Mix Ratio by Weight | 1:1 | resin:hardener | |||