- 弯曲强度 [MPa]: 24.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 80000 cP | 80000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 77 | 77 | |||
| Tensile Strength, Ultimate | 24.1 MPa | 3500 psi | after optimum cure | ||
| Elongation at Break | 11.2 % | 11.2 % | |||
| Adhesive Bond Strength | 27.9 MPa | 4050 psi | Steel-Steel; after optimum cure | ||
| 5.52 MPa @Temperature 82.2 °C | 800 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 21.0 MPa @Temperature -54.4 °C | 3050 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 26.9 MPa @Temperature 25.0 °C | 3900 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 28.0 µm/m-°C @Temperature 20.0 °C | 15.6 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 63.0 °C | 145 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Fast cure is 20 min @ 165°F | |||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Brown | ||||
| Mix Ratio | 2/3 | By Weight | |||