- 密度 [g/cm3]: 1.86
- 弯曲强度 [MPa]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.86 g/cc | 0.0672 lb/in³ | |
| Spiral Flow | 64.0 - 88.0 cm | 25.2 - 34.6 in | 177°C/1000 psi |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | |
| Flexural Strength | 121 MPa | 17500 psi | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.91 @Frequency 1000 Hz | 3.91 @Frequency 1000 Hz | |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | |
| Dissipation Factor | 0.0010 @Frequency 1000 Hz | 0.0010 @Frequency 1000 Hz | |
| Arc Resistance | 190 sec | 190 sec | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 µm/m-°C @Temperature 20.0 °C | 12.2 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 155 °C | 311 °F | |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 193 °C | 340 - 379 °F | Molding temperature |