- 缺口冲击强度: 6.94
- 弯曲强度 [MPa]: 55.2
- 弯曲模量 [MPa]: 8.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.2 MPa | 8000 psi | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1500 ksi | tangent; ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790-1 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | Tangent; ASTM D790-1 |
| Poissons Ratio | 0.30 | 0.30 | ISO 527 |
| Izod Impact, Notched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.08 J/cm | 17.0 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 15.0 kV/mm | 380 kV/in | ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D2303 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C | 20.0 µin/in-°F @Temperature 68.0 °F | Z-direction; ASTM D696 |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature 20.0 °C | 15.0 µin/in-°F @Temperature 68.0 °F | XY-direction; ASTM D696 |
| Specific Heat Capacity | 1.51 J/g-°C | 0.360 BTU/lb-°F | ASTM D1269E |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM D1269E |