- 拉伸强度 [MPa]: 9.136
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 600 cP | 600 cP | B Side | ||
| 800 cP | 800 cP | A Side | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 72 | 72 | ASTM D2240 | ||
| Tensile Strength, Yield | 9.136 MPa | 1325 psi | ASTM D412 | ||
| Elongation at Break | 950 % | 950 % | ASTM D412 | ||
| 100% Modulus | 8.89 GPa | 1290 ksi | ASTM D412 | ||
| 300% Modulus | 11.0 GPa | 1590 ksi | ASTM D412 | ||
| Adhesive Bond Strength | >= 1.72 MPa | >= 250 psi | Wood (no primer), Delamination; ASTM D4541 Elcometer | ||
| 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer | |||
| 2.76 MPa | 400 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer | |||
| >= 6.21 MPa | >= 900 psi | Steel (epoxy primer), Primer Failure; ASTM D4541 Elcometer | |||
| >= 10.3 MPa | >= 1500 psi | Steel (no primer), Substrate Failure; ASTM D4541 Elcometer | |||
| Tear Strength | 80.6 kN/m | 460 pli | ASTM D412 | ||
| Taber Abrasion, mg/1000 Cycles | 22 | 22 | CS17 WHEEL, 1kg per 1000 cycles; ASTM D4060 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | >= 93.3 °C | >= 200 °F | ASTM Pensky-Martin | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 0.267 - 0.583 min | 0.00444 - 0.00972 hour | Tack Free Time | ||
| Gel Time | 0.150 min | 0.150 min | Fast | ||
| 0.366667 min | 0.366667 min | Slow | |||
| Descriptive Properties | |||||
| Color | Most primary colors, including white. | ||||
| Flexibility | Pass | ASTM D1737, 1/8"Mandrel | |||
| Resistance to 1,1,1-Trichlorethane | Conditional | ||||
| Resistance to Acetic Acid (100%) | Conditional | ||||
| Resistance to Acetone | Conditional | ||||
| Resistance to Ammonium Hydroxide (50%) | Recommended Conditional | ||||
| Resistance to Benzene | Conditional | ||||
| Resistance to Brine-Saturated H2O | Recommended | Resistance to Brine-Saturated H2O (310g/l) | |||
| Resistance to Chlorinated H2O | Recommended | ||||
| Resistance to Clorox® (10%) H2O | Recommended | ||||
| Resistance to Diesel Fuel | Recommended Conditional | ||||
| Resistance to Gasoline | Recommended Conditional | ||||
| Resistance to Gasoline/ 5% Methanol | Recommended Conditional | ||||
| Resistance to Gasoline/5% MTBE | Recommended Conditional | ||||
| Resistance to H2O | Recommended | ||||
| Resistance to H2O (14 days at 82°C) | Recommended Conditional | ||||
| Resistance to Hydraulic Fluid (oil) | Recommended Conditional | ||||
| Resistance to Hydrochloric Acid (20%) | Recommended | ||||
| Resistance to Hydrofluoric Acid(10%) | Not Recommended | ||||
| Resistance to Isopropyl Alcohol | Recommended | ||||
| Resistance to Lactic Acid | Recommended Conditional | ||||
| Resistance to MEK | Recommended Conditional | ||||
| Resistance to Methanol | Recommended | ||||
| Resistance to Methylene Chloride | Conditional | ||||
| Resistance to Mineral Spirits | Recommended Conditional | ||||
| Resistance to Motor Oil | Recommended | ||||
| Resistance to MTEB | Conditional | ||||
| Resistance to Muriatic Acid (10%) | Recommended | ||||
| Resistance to NaCl/H2O (10%) | Recommended | ||||
| Resistance to Nitric Acid (20%) | Not Recommended | ||||
| Resistance to Phosphoric Acid (10%) | Recommended | ||||
| Resistance to Phosphoric Acid (50%) | Not Recommended | ||||
| Resistance to Potassium Hydroxide (10%) | Recommended | ||||
| Resistance to Potassium Hydroxide (20%) | Recommended, Discoloration | ||||
| Resistance to Propylene Carbonate | Recommended Conditional | ||||
| Resistance to Skydrol® | Conditional | ||||
| Resistance to Sodium Bicarbonate | Recommended | ||||
| Resistance to Sodium Hydroxide (25%) | Recommended | ||||
| Resistance to Sodium Hydroxide (50%) | Recommended, Discoloration | ||||
| Resistance to Sodium Hypochlorite (10%) | Recommended | ||||
| Resistance to Stearic Acid | Recommended | ||||
| Resistance to Sugar/H2O | Recommended | ||||
| Resistance to Sulfuric Acid (>50%) | Recommended Conditional | ||||
| Resistance to Sulfuric Acid (10%) | Recommended | ||||
| Resistance to Toluene | Recommended | ||||
| Resistance to Trisodium Phosphate | Recommended | ||||
| Resistance to Vinegar/ H2O (5%) | Recommended | ||||
| Resistance to Xylene | Recommended Conditional | ||||