- 拉伸强度 [MPa]: 10.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 1200 cP | 1200 cP | B Side | ||
| 1800 cP | 1800 cP | A Side | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 85 | 85 | ASTM D2240 | ||
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D412 | ||
| Elongation at Break | 800 % | 800 % | ASTM D412 | ||
| 100% Modulus | 9.65 GPa | 1400 ksi | ASTM D412 | ||
| Adhesive Bond Strength | >= 2.76 MPa | >= 400 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer | ||
| Tear Strength | 78.9 kN/m | 450 pli | ASTM D412 | ||
| Taber Abrasion, mg/1000 Cycles | 20.5 | 20.5 | CS17 WHEEL, 1kg per 1000 cycles; ASTM D4060 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | >= 93.3 °C | >= 200 °F | ASTM Pensky-Martin | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | >= 10.0 min | >= 0.167 hour | Tack Free Time | ||
| Gel Time | 5.00 min | 5.00 min | |||
| Descriptive Properties | |||||
| Color | Black, Charcoal Gray, Light Gray | ||||
| Flexibility | Pass | ASTM D1737, 1/8"Mandrel | |||
| Resistance to Acetic Acid (100%) | Recommended | ||||
| Resistance to Brake Fluid (310g/l) | Recommended Conditional | ||||
| Resistance to Clorox® (10%) H2O | Conditional, Discoloration | ||||
| Resistance to Diesel Fuel | Recommended | ||||
| Resistance to Gasoline | Recommended | ||||
| Resistance to H2O | Recommended | ||||
| Resistance to Hydraulic Fluid (oil) | Recommended, Discoloration | ||||
| Resistance to Hydrochloric Acid (10%) | Recommended | ||||
| Resistance to Mineral Spirits | Recommended | ||||
| Resistance to Motor Oil | Recommended, Discoloration | ||||
| Resistance to Muriatic Acid (10%) | Recommended | ||||
| Resistance to NaCl/H2O (10%) | Recommended | ||||
| Resistance to Potassium Hydroxide (10%) | Recommended | ||||
| Resistance to Sodium Bicarbonate | Recommended | ||||
| Resistance to Sodium Hydroxide (10%) | Recommended | ||||
| Resistance to Sugar/H2O | Recommended | ||||
| Resistance to Sulfuric Acid (>22%) | Not Recommended | ||||
| Resistance to Sulfuric Acid (10%) | Recommended, Discoloration | ||||
| Resistance to Vinegar/ H2O (5%) | Recommended | ||||
| Resistance to Xylene | Conditional | ||||