- 吸水率 [%]: 11.0
- 拉伸强度 [MPa]: 14.51
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 11 % | 11 % | 7 days | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 60 | 60 | 12 hours post cure. | ||
| 67 | 67 | 5 seconds, Room Temperature | |||
| 72 | 72 | 1 second, Room Temperature | |||
| Tensile Strength, Yield | 14.51 MPa | 2104 psi | After 28 days, 90°C H2O | ||
| 15.80 MPa | 2291 psi | After 14 days, 90°C H2O | |||
| 16.12 MPa | 2338 psi | 12 hours post cure | |||
| 19.48 MPa | 2826 psi | Room Temperature | |||
| Elongation at Break | 56 % | 56 % | Room Temperature | ||
| 70 % | 70 % | 12 hours post cure | |||
| Tear Strength | 83.6 kN/m | 477 pli | Die C | ||
| 115 kN/m | 654 pli | Die C | |||
| Taber Abrasion, mg/1000 Cycles | 253 | 253 | Room Temperature | ||
| Descriptive Properties | |||||
| Resistance to Chlorinated Water Resistance | +2.7 | Tensile Change (%) | |||
| +5.6 | Tear Strength Change | ||||
| 0 | Elongation Change (%) | ||||
| 0 | Hardness Change | ||||
| Slight Discoloration | Appearance Change | ||||