- 密度 [g/cm3]: 1.24
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 19.0 microns | 0.750 mil | Side 1, Cured Layer; Arlon SQA-TMS-003 | ||
| 19.0 microns | 0.750 mil | Side 2; Arlon SQA-TMS-003 | |||
| 38.1 microns | 1.50 mil | Interleave | |||
| 152 microns | 6.00 mil | Side 1, Uncured Layer; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 394 microns | 15.5 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.07 MPa | 880 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 470 % | 470 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.40 kN/m | 8.00 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM E 1530 | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 - 180 min @Temperature 191 - 210 °C | 2.00 - 3.00 hour @Temperature 375 - 410 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 16 | Arlon SQA-TMS-025 | |||