- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.374
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | ASTM D1895 | ||
| Density | 1.80 g/cc | 0.0650 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D6289 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ASTM D638 | ||
| Tensile Modulus | 17.2 GPa | 2490 ksi | ASTM D638 | ||
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 | ||
| Compressive Strength | 241 MPa | 35000 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.374 J/cm | 0.701 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 4.9 @Frequency 1.00e+6 Hz | 4.9 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 13.8 kV/mm | 351 kV/in | step-by-step; ASTM D149 | ||
| 17.7 kV/mm | 450 kV/in | short time; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | UL Temperature Index; at 3.0 mm | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | ||||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||